Experimental Analysis of Magnetic Particle Inspection on S355J2 Steel Weld Joints

Authors

  • Muhammad Avicena Apriliansyah Universitas Pembangunan Nasional "Veteran" Yogyakarta

DOI:

https://doi.org/10.31315/jmept.v4i1.7813

Keywords:

MPI, S355 J2, WPQR, Welding GMAW, Physical metallurgy

Abstract

NDT (Non-Destructive Test) is a form of testing carried out on materials or objects without causing permanent damage to these materials or objects. This study aims to determine the NDT Magnetic Particle Inspection testing process that is carried out and find out the results of the inspection of S355 J2 steel specimens with the NDT Magnetic Particle Inspection test method as the basis for determining the GMAW Welder Qualification. Welding of S355 J2 Steel is performed by a certified welder using GMAW welding using a single V-butt joint at an angle of 30 degrees. NDT Visual Test and Magnetic Particle Inspection are carried out during material testing. Data & output shows welder PT. INKA qualified with the standards set by the company, namely AWS D1.1 and ASTME E 709. So the Welder can be allowed to work on a Project because it is considered to have met the required Welder qualification standards.

References

Ahmad Abi Sodik1 , Nely Ana Mufarida2 , Kosjoko3. 2019. Pengaruh Penerapan WPS (Welding Procedure Specification) Al 6005 Tipe Butt Joint Terhadap Kekuatan Sambungan Las Al 6061. Jember: Universitas Muhammadiyah jember

Alfian Wahyu Prasetya, 2017 " Pengaruh Debit Gas Pelindung Dan Tegangan Listrik Terhadap Tingkat Kekerasan Dan Struktur Mikro Sambungan Las Gmaw Pada Baja Karbon Sedang Ems-45 " Semarang , Universitas Negeri Semarang.

Alip, M. 1989. Teori dan Praktik Las. Yogyakarta: IKIP Yogyakarta

Amalia, Y., & Rahmatillah, S. (2022). Analisis Sambungan Las Baja S355 J2 Sebagai Penyusun Welding Procedure Specification di PT Industri Kereta Api. JUSTER : Jurnal Sains Dan Terapan, 1(2), 1–6.

A. Ibrahim, S. A. Mohamat, A. Amir, and A. Ghalib, “The Effect of Gas Metal Arc Welding (GMAW) processes on different welding parameters,” Procedia Eng., vol. 41, pp. 1502–1506, 2012.

B. Mvola and P. Kah, “Effects of shielding gas control: welded joint properties in GMAW process optimization,” Int. J. Adv. Manuf. Technol., vol. 88, no. 9–12, pp. 2369– 2387, 2017.

Cecep Slamet Abadi1, Rosidi, Idrus Assagaf . 2019 . " Analisa Kekuatan Welding Repair Baja Aisi 420 Dengan Metoda Gmaw " Politeknologi Vol. 18 No. 3. jakarta. Politeknik Negeri Jakarta

E. Karadeniz, U. Ozsarac, C. Yildiz. 2007, The effect of process parameters on penetration in gas metal arc welding processes. Materials & design, Vol. 28, no. 2: 649-656.

Kholis, Ikhsan. 2012. Kualifikasi Welding Procedure Specification (WPS) dan Juru Las (Welder) Berdasarkan ASME Section IX di Industri Migas. Forum Teknologi, 2(3), 16- 25.

Mujiyanto, Tantok. 2008. Analisis Hasil Pengelasan GMAW Dengan Jenis Ekeltroda ER70S6 di PT INKA Madiun. Madiun: Universitas Merdeka Madiun

Patil, NR. 2008. Non Destructive Testing (NDT) Advantages and limitations. SRES College of Engineering, Kopargaon, Maharastha, 423-603

Rahmatika, Amelia, dkk. 2021. Pengujian Merusak Pada Kualifikasi Prosedur Las Plat Baja Karbon SA-36 dengan Proses Pengelasan SMAW Berdasarkan Standar ASME Section IX. Jurnal Vokasi Teknologi Industri, 3(1), 24-30.

Sri, Widharto. 2013. Welding Inspection. Mitra Wacana Media. Jakarta.

Suwahyo. 2011. Mengelas Dengan Proses Las Busur Listrik Manual. Yogyakarta: PT. Pustaka Insan Madani

Wahyudi, Muhammad Thoriq, dkk. 2015. Modul Praktek Kualifikasi Las. Surabaya: Politeknik Perkapalan Negeri Surabaya.

Downloads

Published

2023-08-23

Issue

Vol 4, No 1 (August 2023)

Section

Articles

License

Authors who publish in Journal of Metallurgical Engineering and Processing Technology agree to the following terms:

  1. Authors who publish articles in this journal agree to the following terms:

    1. Copyright remains with the author and gives rights to the Journal of Metallurgical Engineering and Processing Technology as the priority to publish the article with an Creative Commons Atribusi 4.0 Internasional License, which allows the article to be shared with acknowledgment of the author of the article and this journal as the place of publication.
    2. Authors can distribute the publication of their articles on a non-exclusive basis (for example: on university repositories or books) with notification or acknowledgment of publication in the journal Option
    3. Authors are allowed to post their work online (for example: on personal websites or in university repositories) before and after the submission process (see The Effect of Open Access)

    Journal of Metallurgical Engineering and Processing Technology is licensed under a Creative Commons Atribusi 4.0 Internasional License.