Sintesis Membran Kitosan dengan Crosslinker Kalium Persulfat untuk Pemisahan Zat Warna Rhodamin B

Reka Arumi Anwar, Sekar Kinanti Putri, Endang Sulistyawati

Abstract


Chitosan membrane is a semipermeable porous medium that can separate particles of molecular size in a solution system by filtration and adsorption. Adsorption occurs because chitosan has an amino group (NH3+), so it can adsorb negative ions. Membrane performance can be improved by adding crosslinker potassium persulfate. The test material is Rhodamine B because it has chlorine ion (Cl-) so it can bind to NH3+ on the chitosan membrane. The membrane made by dissolving chitosan powder into 200 mL of 1% acetic acid, then added potassium persulfate with mass variations. Adsorption of Rhodamine B is carried out with a time variation. The relatively good mechanical properties of the membrane can be seen from the results of the Screw Test Stand with stress value 1.9726 MPa and  strain value 2.78%. The performance was relatively good obtained on 0.25 grams of potassium persulfate in 4 grams of chitosan with 75 minutes of adsorption time and was able to reduce the concentration of Rhodamine B from 2.8864 ppm to 1.7477 ppm. The morphological properties shown with the pore size 0.20 µm-1.00 µm and it is classified as ultrafiltration membrane so it can hold Rhodamine B particles with diameter 10 µm.


Keywords


potassium persulfate, chitosan, membrane, Rhodamine B

Full Text:

PDF (Indonesian)

References


Asip, Faisol. Uji Efektifitas cangkang Telur dalam Mengadsorpsi Ion Fe dengan Proses Batch. Palembang: Universitas Sriwijaya. 2008.

Ath Thoriq, Reizal. Pengembangan Kitosan Terkini pada Berbagai Aplikasi Kehidupan. Riau : Fakultas Teknik Universitas Riau. 2008.

Brown, G.G. Unit Operation. New York : John Wiley & Sons, Inc. 1950.

Eckenfelder. Industrial Water Pollution Control. Mc Graw Hill Book Company:Singapore, 2000.

Galih, Trias. Pengaruh Komposisi Blending dan Pelarut Terhadap Kinerja Membran PVDF - Kitosan dalam Pemisahan Pewarna Rhodamin B. Surabaya: FMIPA Universitas Negeri Surabaya. 2015.

Harahap, Yosmarina. Preparasi dan Karakterisasi Nanopartikel Kitosan dengan Variasi Asam. Depok: Fakultas Teknik Universitas Indonesia. 2012.

Hu ZG, Zhang J, Chan WL, Szteto YS. The Sorption of Acid Dye onto Chitosan Nanoparticles. Polym 47. 2006: 5838-5842

Ishihara. Polymer and Crosslinked Body Thereof. US Patent 0051140, 2018

Jaber. Grafted Ultra High Molecular Weight Polyethylene Microporous Membrane. US Patent 0290109, 2018

Kurniasih, Mardiyah. Adsorpsi Rhodamin B dengan Adsorben Kitosan Serbuk dan Beads Kitosan. Purwokerto: FMIPA Universitas Jenderal Soedirman. 2014.

Kusumawati, Nita. Pembuatan dan Uji Kemampuan Membran Kitosan sebagai Membran Ultrafiltrasi untuk Pemisahan Zat Warna Rhodamin B. Surabaya: FMIPA Universitas Negeri Surabaya. 2005.

Mahreni. Batik Warna Alami. Yogyakarta: Universitas Pembangunan Nasional “Veteran” Yogyakarta. 2016.

Maryani, Deni, Ali Masduqi, dan Atik Moesriati. Pengaruh Ketebalan Media dan Rate Filtrasi pada Sand Filter dalam Menurunkan Kekeruhan dan Total Coliform. Fakultas Teknik Sipil dan Perencanaan, Institut Teknologi Sepuluh November. 2014.

Mukherjee, Bharath S. Journal of Lab Model Mechanical Strength Test Instrument for Tensile Strength Determination of Film Formulation. Bangalore: University of Applied Science. 2018.

Mulder, M. Basic Principle of Membran Technology. Kluwer Akademik Publisher: Nedherland, 1996.

Peraturan Menteri Kesehatan Republik Indonesia No.239/Men.Kes/Per/V/85 Tentang Zat Warna Tertentu yang Dinyatakan sebagai Bahan Berbahaya. 2014. www.depkes.go.id. (Diakses tanggal 13 September 2018)

Pitriani, Pipit. Sintesis dan Aplikasi Kitosan dari Cangkang Rajungan sebagai Penyerap Ion Besi dan Mangan untuk Pemurnian Natrium Silikat. Jakarta: UIN Syarif Hidayatullah Jakarta. 2010.

Purnawati. Optimalisasi Adsorpsi Zat Warna Rhodamin B Oleh Biomassa Chlorella Sp dalam Silika Gel. Semarang: Universitas Negeri Semarang. 2011.

Purwantiningsih, Sugita. Kitosan sebagai Sumber Biomaterial Masa Depan. Bogor: FMIPA Institut Pertanian Bogor. 2009.

Setiyanto. Adsorpsi Pewarna Tekstil Rhodamin B Menggunakan Senyawa Xanthat Pulpa Kopi. Semarang: Universitas Wahid Hasyim Semarang. 2015

Singh, V., Sharma AK, Tripathi DN, Sanghi R. 2008. Poly (methylethacrylate) Grafted Chitosan an Efficient Adsorbent for Anionic Azo Dyes. Hazard Matter.2008; 96 (04)

Wahyuni, Sri. Pengaruh Konsentrasi dan Kecepatan Pengadukan Terhadap Karakteristik Membran Komposit Kitosan. Surabaya: Institut Teknologi Sepuluh November Surabaya. 2016


Refbacks

  • There are currently no refbacks.